Solid wire which gives fully austenitic niobium stabilized weld deposit. The wire contents low level of S, Si, P & S which reduces hot cracking tendency and fissuring. The wire gives a low carbon nil ferrite “super-austenitic” weld metal with good resistance to attack by a range of organic and inorganic acids, sulphuric and minerals acids etc.
Deposited weld metal which is fully austenitic, has controlled level of phosphorus and silicon which helps to eliminate solidification cracking tendency.
WELDING CURRENT: DC( - )
SHIELDING GAS: Pure Argon 99.9% 6-12 l/mn.
|0.025 max||1.50 - 2.0||0.15 max||0.015 max||0.015 max||19.0-21.0||32 -36||2.0-3.0||3.0-4.0||8XC% min or 0.40 max|
|Tensile Strength MPa||Yield Stress MPa||Elongation (%) (L=4D)|
|520 min||350 min||35 min|
|SIZE (mm)||LENGTH (mm)||PACKING PER BOX|