Weldable in all positions. Arc striking and rearc striking properties are excellent. Arc is soft & stable. The spatter is very low and the slag is easy to remove. The weld deposits is free from cracks & porosity. The weld bead is fine, rippled, smooth and regular.
Austenitic manganese steel to mild steel and weld metal has excellent heat resistant properties upto 9000 C. it is applicable for crack free joints in difficult steel & armow steel.
Specially designed for joining austenitic manganese steel (12% Mn) to mild steel & for producing crack free joints in difficult steels, low alloy & high alloy steels including armow plate. Excellent for repairing cracks in austenitic manganese steel points & crossings, & laying buffer layer on difficult steels before hardfacing.
|0.12 max||5.00-7.00||0.30-0.8||0.03 max||0.03 max||18.0-21.0||8.50-11.0|
The base metal should be free from oil grease or dirt before welding. Keep a short arc length. The weld bead should be cleaned properly with stainless steel brush and ensure proper fitup on joints. Do not use more than recommended current limit. Redry electrode at 300° C ihr to better result.
|Tensile Strength Mpa||Elongation (%) (L=4D)||Charpy V-Notch Impact Value|
|SIZE (mm)||LENGTH (mm)||AMPS||POLARITY||WT PER CARTON||WT PER BOX|